Nickel 201 Alloy Uns N02201/2.4061 Nickel Alloy Steel Seamless Tube Heat Exchanger Tube, Bolier Tube

• Customization: Available
• Type: Round
• Standard: AISI, ASTM, DIN, JIS, GB, BS
• Model NO.: OD: 1/2"--18", WT: 10S--XXS
• Composition: Stainless Steel Scrap
• Technique: Cold Drawn
• Shape: Round
• Surface Treatment: Annealing & Pickling
• Special Use: Heat Exchanger Tube, Bolier Tube
• Application: Anti-Acid
• Transport Package: Plywood Case
• Specification: OD: 1/2"--12", WT: 10S--XXS
• Trademark: XTD
• Origin: China
• HS Code: 75071200
• Production Capacity: 1000 Tons Per Year

Product Description

 

PIPE & TUBE STANDARD:
ASTM B161/ ASTM B163/ ASTM B167/ ASTM B444/ ASTM B622 ...

OD RANGE :
6-457 MM

THICKNESS RANGE:
1-45 MM

Chemical Composition

 

Grade	Ni	Cu	Fe	Mn	C	Si	S
UNS N02201	≥99.01	≤0.25	≤0.40	≤0.35	≤0.02	≤0.35	≤0.01

Note:
1.Element shall be determined arithmetically by difference.

 

Mechanical Properties

Grade	Condition	Tensile Strength	Yield Strength	Elongation(%)
N02201	Annealed	≥50(345)ksi(MPa)	≥12(83)ksi(MPa)	≥40
N02201	Stress-relieved	≥60(414)ksi(MPa)	≥30(207)ksi(MPa)	≥15
N02201 OD≤127MM	Annealed	≥50000(380)psi(MPa)	≥12000(80)psi(MPa)	≥35
N02201 OD>127MM	Annealed	≥50000(345)psi(MPa)	≥10000(70)psi(MPa)	≥40
N02201	Stress-relieved	≥60000(415)psi(MPa)	≥30000(205)psi(MPa)	≥15

Applications

Used primarily for parts requiring excellent corrosion and strong magnetic properties such as:

• lead wires
• battery components
• transducers
• sparking electrodes
• heat exchangers
• implantable battery anode/connector tabs for CRM and Neurostimulation devices
• stamped or etched fabrications

Material Summary

Nickel 201 alloy is a commercially pure wrought alloy having properties similar to that of nickel 200 alloy, but with a lower carbon content to avoid embrittlement by inter-granular carbon at high temperatures.

It is resistant to acids and alkalis, and dry gases at room temperature.

Alloy 201 is a wrought commercially pure Nickel with a maximum carbon level of 0.02%. This alloy provides highly ductile mechanical properties across a wide temperature range.It provides corrosion resistance in neutral to moderately reducing environments. Nickel 201 is ferromagnetic. It provides high thermal and electrical conductivity in comparison to nickel-base alloys, stainless and low alloy steels. Because of its low carbon content (.02% max.) Nickel 201 may be considered for service above 600 °F (316 °C), where alloy 200 with higher carbon content is not recommended.