Tp316ti 1.4571 Uns S31635 Seamles Stainless Steel Pipe and Tube ASTM A312, A269, A213, A240, GOST9941-81, En10216-5

• Type: Seamless
• Technique: Cold Rolled
• Material: Stainless Steel
• Surface Treatment: Pickling and Annealing
• Usage: Pipeline Transport, Boiler Pipe, Hydraulic/Automobile Pipe, Oil/Gas Drilling, Food/Beverage/Dairy Products, Machinery Industry, Chemical Industry, Mining, Construction & Decoration, Special Purpose
• Section Shape: Round
• Model NO.: OD: 1/4"--40", WT: 10S--XXS.
• Transport Package: Knitting Strips, Plywood Case
• Specification: OD: 1/4"--40", WT: 10S--XXS
• Trademark: XTD
• Origin: China
• HS Code: 7304419000
• Production Capacity: 15000 Tons/Year

Product Description

Chemical Composition

Grade	C	Mn	P	S	Si	Cr	Ni	Mo	N	Other
316	≤0.08	≤2.0	≤0.045	≤0.03	≤1.0	16.0-18.0	10.0-14.0	2.0-3.0	-	-
316L	≤0.035	≤2.0	≤0.045	≤0.03	≤1.0	16.0-18.0	10.0-14.0	2.0-3.0	-	-
316H	0.04-0.10	≤2.0	≤0.045	≤0.03	≤1.0	16.0-18.0	11.0-14.0	2.0-3.0	-	-
316Ti	≤0.08	≤2.0	≤0.045	≤0.015	≤0.75	16.0-18.0	10.0-14.0	2.0-3.0	≤0.1	Ti:5×(C%+N)-0.7
316N	≤0.08	≤2.0	≤0.045	≤0.03	≤2.0	16.0-18.0	10.0-13.0	2.0-3.0	0.1-0.16	-
316LN	≤0.035	≤2.0	≤0.045	≤0.015	≤0.015	16.0-18.0	10.0-13.0	2.0-2.5	0.1-0.16	-

Mechanical Properties

Grade	Tensile Strength ksi(MPa)	Yield Strength ksi(MPa)	Elongation,%	Hardness Brinell/Vickers	Hardness Rockwell
316	≥75(515)	≥30(205)	≥35	≤192HBW/200HV	≤90HRB
316L	≥70(485)	≥25(170)	≥35	≤192HBW/200HV	≤90HRB
316H	≥75(515)	≥30(205)	≥35	≤192HBW/200HV	≤90HRB
316Ti	≥75(515)	≥30(205)	≥35	≤192HBW/200HV	≤90HRB
316N	≥80(550)	≥35(240)	≥35	≤192HBW/200HV	≤90HRB

Applications

• Food processing equipment Brewery equipment,
• Chemical and petrochemical equipment,
• Laboratory benches and equipment
• Beach deck coverings,
• Shoreline covers,
• Boat fasteners,
• Chemical containers,
• Heat exchangers,
• Mining sieve,
• Springs,
• Medical implants.

Material Summary

TP316Ti /1.4571/UNSS31635, is a titanium-stabilized, molybdenum-alloyed austenitic chromium-nickel steel with improved machinability has similar characteristics to AISI 316L, but the TP 316Ti has better mechanical properties and strength at high temperatures. TP 316Ti (1.4571, UNS S31635) due to the addition of titanium shows higher corrosion resistance.

TP 316Ti (1.4571, UNS S31635) is generally considered but is not resistant to hot sea water. Hot chloride environments may cause pitting and crevice corrosion. TP 316Ti (1.4571, UNS S31635) HEAT RESISTANCE 316 exhibits good resistance to oxidation in continuous service to a temperature of 870 ° C and a temperature of 925 ° C. However, if corrosion resistance to water is required, continuous use at 425-860 ° C is not recommended. In this case, 316L is recommended due to resistance to carbide precipitation. When high temperatures are required at temperatures above 500 ° C, class 316H is recommended.