Grade |
Ni |
Cu |
Fe |
Mn |
C |
Si |
S |
UNS N02201 |
≥99.01 |
≤0.25 |
≤0.40 |
≤0.35 |
≤0.02 |
≤0.35 |
≤0.01 |
Grade |
Condition |
Tensile Strength |
Yield Strength |
Elongation(%) |
N02201 |
Annealed |
≥50(345)ksi(MPa) |
≥12(83)ksi(MPa) |
≥40 |
N02201 |
Stress-relieved |
≥60(414)ksi(MPa) |
≥30(207)ksi(MPa) |
≥15 |
N02201 OD≤127MM |
Annealed |
≥50000(380)psi(MPa) |
≥12000(80)psi(MPa) |
≥35 |
N02201 OD>127MM |
Annealed |
≥50000(345)psi(MPa) |
≥10000(70)psi(MPa) |
≥40 |
N02201 |
Stress-relieved |
≥60000(415)psi(MPa) |
≥30000(205)psi(MPa) |
≥15 |
Used primarily for parts requiring excellent corrosion and strong magnetic properties such as:
Nickel 201 alloy is a commercially pure wrought alloy having properties similar to that of nickel 200 alloy, but with a lower carbon content to avoid embrittlement by inter-granular carbon at high temperatures.
It is resistant to acids and alkalis, and dry gases at room temperature.
Alloy 201 is a wrought commercially pure Nickel with a maximum carbon level of 0.02%. This alloy provides highly ductile mechanical properties across a wide temperature range.It provides corrosion resistance in neutral to moderately reducing environments. Nickel 201 is ferromagnetic. It provides high thermal and electrical conductivity in comparison to nickel-base alloys, stainless and low alloy steels. Because of its low carbon content (.02% max.) Nickel 201 may be considered for service above 600 °F (316 °C), where alloy 200 with higher carbon content is not recommended.