ASTM/AISI/DIN/JIS, Tp316L/S31603/1.4404/X 2crnimo17-12-2/022cr17ni12mo2 Seamless Austenitic Stainless Steel Pipe

• Customization: Available
• Type: Seamless
• Technique: Cold Rolled
• Model NO.: OD: 1/2"--40", WT: 10S--XXS
• Material: Stainless Steel
• Surface Treatment: Pickling and Annealing
• Usage: Pipeline Transport, Boiler Pipe, Hydraulic/Automobile Pipe, Oil/Gas Drilling, Food/Beverage/Dairy Products, Machinery Industry, Chemical Industry, Mining, Construction & Decoration, Special Purpose
• Section Shape: Round
• Transport Package: Knitting Strips, Plywood Case
• Specification: OD: 1/2"--40", WT: 10S--XXS
• Trademark: XTD
• Origin: China
• HS Code: 7304419000
• Production Capacity: 15000 Tons/Year

Product Description

 

Stainless Steel 316 Pipe is an austenitic stainless steel grade pipe that has good resistance to chloride ion corrosion stress cracking. For this reason, the pipe is used in marine and sea water applications with ease. Zhejiang Xintongda Special Steel Manufacturing Co.,Ltd is a leading supplier and manufacturer of the Stainless Steel 316 Pipe products in various scales and dimensions.

Heat Resistance

Good oxidation resistance in intermittent service to 870°C and in continuous service to 925°C. Continuous use of 316 in the 425-860°C range is not recommended if subsequent aqueous corrosion resistance is important.
Grade 316L is more resistant to carbide precipitation and can be used in the above temperature range.
Grade 316H has higher strength at elevated temperatures and is sometimes used for structural and pressure-containing applications at temperatures above about 500°C.

Hot and Cold Working

316L stainless steel can be hot worked using most common hot working techniques. Optimal hot working temperatures should be in the range 1150-1260°C, and certainly should not be less than 930°C. Post work annealing should be carried out to induce maximum corrosion resistance.
Most common cold working operations such as shearing, drawing and stamping can be performed on 316L stainless steel. Post work annealing should be carried out to remove internal stresses.

 

Chemical Composition

Grade	C	Mn	Si	P	S	Cr	Mo	Ni	Other
316	≤0.08	≤2.0	≤1.0	≤0.045	≤0.03	16.0-18.0	2.0-3.0	11.0-14.0	-
316L	≤0.035	≤2.0	≤1.0	≤0.045	≤0.03	16.0-18.0	2.0-3.0	10.0-14.0	-
316H	0.04-0.10	≤2.0	≤1.0	≤0.045	≤0.03	16.0-18.0	2.0-3.0	11.0-14.0	-
316Ti	≤0.08	≤2.0	≤0.03	≤0.045	≤0.015	16.0-18.0	2.0-3.0	10.0-12.0	Ti5×C%- 0.7
316N	≤0.08	≤2.0	≤2.0	≤0.045	≤0.03	16.0-18.0	2.0-3.0	11.0-14.0	N 0.10-0.16
316LN	≤0.03	≤2.0	≤0.015	≤0.045	≤0.015	16.0-18.0	2.0-2.5	11.0-14.0	N 0.10-0.16

Mechanical Properties

Grade	Tensile Str (MPa) min	Yield Str 0.2% Proof (MPa) min	Elong (% in 50 mm) min	Hardness
				Rockwell B (HR B) max	Brinell (HB) max
316	515	205	40	95	217
316L	485	170	40	95	217
316H	515	205	40	95	217

Physical Properties

Grade	Density (kg/m3)	Elastic Modulus (GPa)	Mean Co-eff of Thermal Expansion (µm/m/°C)			Thermal Conductivity (W/m.K)		Specific Heat 0-100°C (J/kg.K)	Elec Resistivity (nΩ.m)
			0-100°C	0-315°C	0-538°C	At 100°C	At 500°C
316/L/H	8000	193	15.9	16.2	17.5	16.3	21.5	500	740

Grade Specification Comparison

Grade	UNS	EN		DIN		GB	JIS
		BS	EN	No	Name
316L	S31603	316S11	-	1.4404	X2CrNiMo17-12-2	00Cr17Ni13Mo2	SUS 316L

 

Applications

Typical applications include:

• Food preparation equipment particularly in chloride environments.
• Pharmaceuticals
• Marine applications
• Architectural applications
• Medical implants, including pins, screws and orthopaedic implants like total hip and knee replacements
• Fasteners